Orfibrace - 3.0mm (1/8")
| Thickness |
mm (inches) |
3.0 (1/8") |
3.0 (1/8") |
| Perforation |
% (type) |
0 (non perfo) |
1 (macro) |
Thermoforming conditions |
| Optimum activation temperature (in water bath) |
°C (°F) |
65 (149) |
65 (149) |
| Activation time (in water bath) |
min |
3 - 4 |
3 - 4 |
| Transparent when activated |
|
no |
no |
| Working time |
min |
1 - 1 1/2 |
1 - 1 1/2 |
| Hardening time |
min |
6 - 6 1/2 |
5 3/4 - 6 1/4 |
| Time to completion |
min |
24 - 25 |
22 - 23 |
| Resistance to stretch |
|
high |
high |
| Drape |
|
moderate |
moderate |
| Memory (after 200% elongation) |
|
moderate |
moderate |
| Maximum elongation when activated |
% |
2500 |
1800 |
| Memory (after maximum elongation) |
|
moderate |
moderate |
| Sticks to itself when activated and wet |
|
no |
no |
| Sticks to itself when activated, after drying |
|
temporarily |
temporarily |
| Adhesion (velco strip) using heat gun |
|
no |
no |
Mechanical properties at 21°C (70°F) |
| Flexural modulus |
MPa |
700 |
650 |
| Elastic modulus |
MPa |
340 |
340 |
| Tensile strength |
MPa |
17.0 |
13.0 |
| Strain at break |
% |
no break |
60 |
| Shore D hardness |
|
59 |
59 |
General properties |
| Density |
g cm³ |
1.21 |
1.21 |
| Surface feeling |
|
smooth |
smooth |
| Color |
|
grey |
grey |
| Odor |
|
none |
none |
| Fatigue |
cycles |
n.a. |
n.a. |
| Biocompatible |
|
yes |
yes |