Orfit Eco - 2.4mm (3/32")
| Thickness |
mm (inches) |
2.4 (3/32") |
2.4 (3/32") |
| Perforation |
% (type) |
0 (non perfo) |
3.5 (mini) |
Thermoforming conditions |
| Optimum activation temperature (in water bath) |
°C (°F) |
65 (149) |
65 (149) |
| Activation time (in water bath) |
min |
3 - 4 |
3 - 4 |
| Transparent when activated |
|
no |
no |
| Working time |
min |
1 3/4 - 2 1/4 |
1 1/2 - 2 |
| Hardening time |
min |
4 1/4 - 4 3/4 |
4 - 4 1/2 |
| Time to completion |
min |
17 - 18 |
16 - 17 |
| Resistance to stretch |
|
high |
high |
| Drape |
|
high |
high |
| Memory (after 200% elongation) |
|
high |
high |
| Maximum elongation when activated |
% |
450 |
170 |
| Memory (after maximum elongation) |
|
high |
high |
| Sticks to itself when activated and wet |
|
no |
no |
| Sticks to itself when activated, after drying |
|
reliable under low stress |
reliable under low stress |
| Adhesion (velco strip) using heat gun |
|
no |
no |
Mechanical properties at 21°C (70°F) |
| Flexural modulus |
MPa |
575 |
470 |
| Elastic modulus |
MPa |
420 |
365 |
| Tensile strength |
MPa |
15.0 |
11.0 |
| Strain at break |
% |
415 |
40 |
| Shore D hardness |
|
58 |
58 |
General properties |
| Density |
g cm³ |
1.25 |
1.25 |
| Surface feeling |
|
smooth |
smooth |
| Color |
|
off-white, white/grayish |
off-white, white/grayish |
| Odor |
|
none |
none |
| Fatigue |
cycles |
n.a. |
n.a. |
| Biocompatible |
|
yes |
yes |
« Back